MAXAMID PA66-MOS2 BK

Nylon Type 66, 2% Molybdenum Disulfide Resin

 

MAXAMIDPA66-MOS2 is a Nylon 66 with 2% MoS2 incorporated to provide excellent lubricity which significantly reduces the friction and improves the wear properties of injection molded parts.

 

 

Property

 

Test Method

 

Units

Value

DAM

 

Mechanical

Tensile Strength

Elongation @ Break

Flexural Modulus

Flexural Strength

Izod Impact

 

 

 

ASTM D 638

ASTM D 638

ASTM D 790

ASTM D 790

ASTM D256

 

 

 

Mpa (psi)

%

Mpa (psi)

Mpa (psi)

J/m (ft lb/in)

 

 

 

82.8 (12,000)

20

3448 (500,000)

137.9 (20,000)

48 (.9)

 

 

Thermal

Heat Deflection Temperature

1.8 Mpa (264 psi)

Melting Point

 

 

 

ASTM D 648

 

ASTM D 3418

 

 

C (F)

 

C (F)

 

 

 

 

183 (361)

259 (498)

 

Other

Specific Gravity

 

 

ASTM D 792

 

 

 

 

 

1.16

 

 

Processing

Melt Temperature Range

Mold Temperature Range

Processing Moisture Content

 

 

 

 

C (F)

C (F)

%

 

 

290-305 (550-580)

38-93 (100-200)

<0.20

 

 

Mechanical properties measured at 23C (73F)

Contact Pier One Polymers for MSDS, general guidelines and/or additional information about ventilation, handling, purging, drying, etc.

 

 

CALL PIER ONE POLYMERS FIRST (877) 283-1975

 

 

 

                                                                                                                                                                                                                                         

The information above is compiled by the material manufacturer. Actual values should not be construed as a guarantee of analysis of any specific lot or as specification items. The properties of any single lot or shipment of product may vary from the above analysis. No warranty is given as to the suitability of the product for any particular application. The determination of suitability of the above product information for any particular use is solely the responsibility of the user.